Alloy L-605 (Alloy 25)

Chemical Composition Limits
Weight %	C	P	Si	Ni	W	Mn	S	Cr	Co	Fe
Alloy L-605	0.05 -0.15	0.030 max	0.40 max	9.0- 11.0	14.0- 16.0	1.0- 2.0	0.030 max	19.0- 21.0	Bal	3.0 max

Alloy Alloy L-605 (Alloy 25) is a non-magnetic chromium, nickel, tungsten, cobalt alloy. L-605 has excellent high temperature strength and good oxidation resistance to 2000ºF (1093ºC). L-605 is used in gas turbines rotors, combustion chambers, various industrial furnace applications and in the medical industry in heart valves.

Availability

Alloy L-605 (Alloy 25) is available in Bar (Rounds), Rod, Wire, Sheet, Strip, Forging Stock, Foil, Welding Wire, Billet and L- 605 Vac Melt Bar. For all stock availability contact Sales.

Specifications

UNS R30605

AMS 5759F Bar and Forging Stock

ASTM F90 Bar and Wire (All implant quality)

AMS 5507 Sheet Strip and Plate

AMS 5796 Welding Wire

AMS 5797 (UNS W73605) Welding Rod

Typical Room Temperature Mechanical Properties

Alloy L-605 Bar (Alloy 25)
Condition	Diameter or Thickness mm	Tensile Strength Mpa	0.2% Offset Yield Strength Mpa	Elongation (%) (x 4D)	Reduction of Area %
Annealed	> 1.6 mm	917	476	41	33
Cold Worked 30%	1.6 -9.5 mm	1345	1000	16	18

Disclaimer

Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.