Data Sheet:

Alloy X-750 

Alloy X-750
Weight % Ni + (Co) Cr Fe Ti Al Nb +(Ta) Mn Si S Cu C Co

X-750

UNS N07750

 70 min 14-17 5-9 2.25- 2.75 0.40- 1.0 0.70 -1.2 1 max 0.50 max 0.01 max 0.50 max 0.08 max 1 max

UNS N07752 is available in billets for forging.  UNS N0772 has limits of 0.05% on both Carbon and Cobalt.  

 

Alloy X-750 is a nickel-chromium alloy which has been made precipitation-hardenable by the additions of aluminum and titanium.  Alloy X-750 has good resistance to corrosion and oxidation along with high tensile and creep rupture properties at temperature up to 1300ºF (700ºC).  Due to X-750's excellent relaxation resistance it is useful for applications as high-temperature springs and bolts, X-750 is also used in gas turbines, rocket engines, nuclear reactors, pressure vessels, tooling and aircraft structures.

  

Availability

Alloy X-750  is available in  Round Bar, Flat Bar, Sheet, Strip, Plate, Forging Stock, Hexagon, Wire, Tube, Welding Wire and Extruded Section .  Ex-stock is available in Round Bar - Equalized or Sheet & Plate.  For all stock availability contact Sales.

  

Specifications

Rod ASTM B 637, ASME SB 637, ISO 9723, ISO9724, ISO9725, AMS 5667, AMS 5668, AMS 5669, AMS 5670, AMS 5671, AMS 5747, EN10269
Bar ASTM B 637, ASME SB 637, ISO 9723, ISO9724, ISO9725, AMS 5667, AMS 5668, AMS 5669, AMS 5670, AMS 5671, AMS 5747, EN10269
Forging Stock ASTM B 637, ASME SB 637, ISO 9723, ISO9724, ISO9725, AMS 5667, AMS 5668, AMS 5669, AMS 5670, AMS 5671, AMS 5747, EN10269
Plate ISO 6208, AMS 5542 and AMS 5598
Sheet ISO 6208, AMS 5542 and AMS 5598
Strip ISO 6208, AMS 5542 and AMS 5598
Wire BS HR 505, AMS 5698, AMS 5699
Other UNS N07750, W.Nr 2.4669, Inconel X750 (tradename), UNS N07752

  

Rod, Bars and Forgings are available with the following heat treatments 

 

AMS 5667 - 1625°F/24hr, AC + 1300°F/20 hr, AC (Equalising plus precipitation treatment).  AMS 5667 Rod, Bars and Forgings have high strength and notch rupture ductility up to 1100°F

 

AMS 5668 - 2100°F anneal + 1550°F/24 hr, AC, +1300°F/20hr, AC (triple heat treatment).  AMS 5668 has maximum creep, relaxation and rupture strength above about 1100°F.  

 

AMS 5670 - 1800°F anneal + 1350°F/8hr, FC to 1150°F.  Hold at 1150°F for total precipitation-treating time 18 hr, AC (solution treatment plus furnace cool precipitation treatment).  Due to the heat treatments AMS 5670, AMS 5671 and AMS 5747 have increased tensile properties and reduced heat treatment time service up to about 1100°F.

 

With a heat treatment of 1800°F anneal + 1400°F/1hr, FC to 1150°F, hold at 1150°F for total precipitation-treating time of 6 hr, AC (solution treatment plus short furnace-cool precipitation treatment).  This treatment of short furnace cool aging achieves only slightly lower properties than does AMS 5670 and AMS 5671.

 

Rods and Bars X-750 is available from 1/2" diameter to 6" diameter in 1/4" increments. From 6" diameter to 10" diameter it is available in 1/2" increments. 

 

Billets for forging are available heat treated to any specification.

 

UNS N07752 is available in billet for forging. UNS N07752 has limits on the Carbon and Cobalt levels (each has a maximum of 0.05%).

 

Sheet, Strip and Plate are available with the following heat treatments

 

AMS 5542 - 1300°F/20hr, AC (Constant-temperature precipitation treatment).  AMS 5542 has high strength up to 1300°F

 

AMS 5598 - 1350°F/8hr, FC to 1150°F, hold at 1150°F for total precipitation-treating time of 18hr, AC (furnace-cool precipitation treatment.  AMS 5598 has high strength up to 1300°F (Increased tensile properties to about 1100°F).

 

With heat treatment 1400°F/1hr, FC to 1150°F hold at 1150°F for total time of 6hr, AC (short furnace-cool precipitation treatment).  This treatment enables increased tensile properties and reduced heat time for service up to about 1100°F.

 

TYPICAL MECHANICAL PROPERTIES

Size

Ultimate Tensile Strength (ksi)

0.2% Yield Strength (ksi)

Elongation in 4D(%)

% Reduction of Area
Under 4.0" 165.0 105 20 25
4.0" and over 160.0 100 15 17

Properties as described in AMS 5667 which requires that material following 1625ºF/24 hr, AC - Equalizing have the following minimum room temperature properties.  Hardness will lie in the range of 302-363 BHN.

  

Disclaimer    

Every effort is made to ensure that technical specifications are accurate. However, technical specifications included herein should be used as a guideline only. All specifications are subject to change without notice.

   

Sell your Surplus Stock Online at 4metal.co.uk

  

Sales Enquires : sales@aircraftmaterialsuk.com

Site © 2001 AirCraftMaterialsUK.com Ltd,Unit C5, Regent Park, Princes Estate, Princes Risborough, Buckinghamshire, HP27 9LE, UK

Tel: 44(0)1844 275560 Fax: 44(0)1844 346892 

Group companies Quantum Alloys Ltd